| Molecular Formula | C43H64O10 |
| Molar Mass | 740.98 |
| Density | 1.16±0.1 g/cm3(Predicted) |
| Melting Point | 125 °C |
| Boling Point | 755.7±55.0 °C(Predicted) |
| Solubility | Acetonitrile (Slightly), DMSO (Slightly) |
| Appearance | Solid |
| Color | White to Off-White |
| pKa | 11.44±0.25(Predicted) |
| Storage Condition | Inert atmosphere,Room Temperature |
| Hazard Symbols | Xn - Harmful![]() |
| Risk Codes | 21 - Harmful in contact with skin |
| Safety Description | 36/37 - Wear suitable protective clothing and gloves. |
| EPA chemical substance information | information provided by: ofmpeb.epa.gov (external link) |
| preparation | The PPS Resin was dried under vacuum at 120 °c for 12 h, and then in accordance with 0. 5%, 1. 0%, 3. 0% and 5. 0 %(mass fraction, the same below) mixing ratio of the antioxidant GA 80 and PPS Resin are mixed evenly, and then the micro twin-screw extruder is used for melt blending and extrusion, the partition temperature of the screw extruder was 280, 285, 290 ℃, the blending time was 3 min, and the screw speed was 25 r/min, where x is the content of the antioxidant GA Δ80. |
| effect | The antioxidant GA Δ80 has good compatibility with PPS, and can be uniformly dispersed in the PPS matrix, when the content of GA +80 is more than or equal to 3. 0%, GA 80 will produce partial agglomeration. |